When early cannon barrels of cast iron experienced catastrophic failure, which mechanism triggered the explosions?

💡 Explanation

Hydrogen embrittlement weakens iron because atomic hydrogen diffuses into the iron's lattice, accumulating at grain boundaries, therefore reducing its ductility and fracture toughness, rather than oxidation, corrosion, or exceeding the tensile strength from simple thermal stress.

• Post-Medieval European masonry frequently relied on 'hydraulic lime' mortars; which consequence arose if insufficiently burned?
• Which consequence results from inaccuracies in Ptolemy's geocentric model when predicting planetary positions?
• Which risk increased in the Uruk period when early Mesopotamian bronze chisels encountered harder stones?
• On a wooden-hulled 18th-century ship crossing the Atlantic, which outcome increases risk when differential thermal expansion changes a sextant's calibration?
• Which outcome inhibits crop growth when terrace farming experiences prolonged, heavy rainfall?
• Which outcome occurs when gravity-fed 'chadar' (water cascade) systems supporting Mughal gardens develop a blockage?