Which consequence results when residual shell material remains during investment casting?

💡 Explanation

Increased surface porosity occurs because the shell fragments inhibit complete metal flow during solidification. This "Slag entrapment" defects surface integrity; therefore porosity results, rather than improved casting dimensions given unobstructed flow.