Which mechanism drives mechanical failure when cyclic stress exceeds a crystal's fatigue limit?

💡 Explanation

Dislocation pile-up at grain boundaries causes fatigue cracks because dislocations cannot cross the boundary, therefore embrittling the material, rather than vacancy diffusion which is thermally activated at higher temperatures.