Which microstructural defect directly results from eutectic casting's undercooling?

💡 Explanation

Dendrite arm spacing varies during undercooling in eutectic casting because non-equilibrium solidification advances at fluctuating rates, leading to uneven solute distribution therefore varying arm spacings develop, rather than uniform phases transformations/boundaries/porosity during proper cooling.