Which outcome occurs when rapid cycling induces hydrogen absorption in a palladium membrane?

💡 Explanation

Extensive charging and discharging leads to hydrogen embrittlement because repeated lattice expansion/contraction induces microcrack propagation. Therefore, fracture toughness reduces rather than other properties altering significantly without sustained annealing at high temperatures.